ATI Allegheny Ludlum 430 Ferritic Stainless Steel

Category Metal , Ferrous Metal , Ferritic , Stainless Steel , T 400 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum 430 Ferritic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:oxidation resistant at elevated temperatures, corrosion resistance approaching nickel-bearing stainless steels in mildly corrosive environments, ductile, does not work harden readily. Forms:plates, sheets, strip, foil.Applications:interior and exterior trim, sinks, counter tops, dish washers, range hoods, flatware, roofing, siding, and restaurant equipment.Information provided by Allegheny Ludlum
Physical Properties Metric English Comments
Specific Gravity 7.70 g/cc
7.70 g/cc
Density 7.70 g/cc
0.278 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 75 - 83

@Thickness 1.02 - 2.92 mm
 75 - 83

@Thickness 0.0400 - 0.115 in
Hardness, Rockwell 30T 62 - 70

@Thickness 0.508 - 1.52 mm
 62 - 70

@Thickness 0.0200 - 0.0600 in
Tensile Strength, Ultimate 455 - 538 MPa

@Thickness 1.02 - 2.92 mm
 66000 - 78000 psi

@Thickness 0.0400 - 0.115 in
483 - 545 MPa

@Thickness 0.508 - 1.52 mm
 70100 - 79000 psi

@Thickness 0.0200 - 0.0600 in
Tensile Strength, Yield 303 - 372 MPa

@Strain 0.200 %,
Thickness 0.508 - 1.52 mm
 43900 - 54000 psi

@Strain 0.200 %,
Thickness 0.0200 - 0.0600 in
296 - 386 MPa

@Strain 0.200 %,
Thickness 1.02 - 2.92 mm
 42900 - 56000 psi

@Strain 0.200 %,
Thickness 0.0400 - 0.115 in
Elongation at Break 21 - 34 %

@Thickness 0.508 - 1.52 mm
 21 - 34 %

@Thickness 0.0200 - 0.0600 in
23 - 37 %

@Thickness 1.02 - 2.92 mm
 23 - 37 %

@Thickness 0.0400 - 0.115 in
Creep Strength 6.90 MPa

@Temperature 760 °C,
Time 3.60e+7 sec
 1000 psi

@Temperature 1400 °F,
Time 10000 hour
69.0 MPa

@Temperature 538 °C,
Time 3.60e+7 sec
 10000 psi

@Temperature 1000 °F,
Time 10000 hour
Fatigue Strength 159 - 243 MPa

@# of Cycles 1.00e+7
23100 - 35200 psi

@# of Cycles 1.00e+7
Thermal Properties Metric English Comments
CTE, linear 10.3 µm/m-°C

@Temperature 20.0 - 100 °C
 5.72 µin/in-°F

@Temperature 68.0 - 212 °F
11.2 µm/m-°C

@Temperature 20.0 - 500 °C
 6.22 µin/in-°F

@Temperature 68.0 - 932 °F
11.9 µm/m-°C

@Temperature 20.0 - 787 °C
 6.61 µin/in-°F

@Temperature 68.0 - 1450 °F
Specific Heat Capacity 0.460 J/g-°C

@Temperature 0.000 - 100 °C
 0.110 BTU/lb-°F

@Temperature 32.0 - 212 °F
Thermal Conductivity 23.86 W/m-K

@Temperature 20.0 - 100 °C
 165.6 BTU-in/hr-ft²-°F

@Temperature 68.0 - 212 °F
25.96 W/m-K

@Temperature 20.0 - 500 °C
 180.2 BTU-in/hr-ft²-°F

@Temperature 68.0 - 932 °F
Melting Point 1425 - 1510 °C
2597 - 2750 °F
Solidus 1425 °C
2597 °F
Liquidus 1510 °C
2750 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.12 %
<= 0.12 %
Chromium, Cr 16 - 18 %
16 - 18 %
Iron, Fe >= 79.31 %
>= 79.31 %
As Remainder
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo <= 0.50 %
<= 0.50 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000600 ohm-cm

@Temperature 20.0 °C
 0.0000600 ohm-cm

@Temperature 68.0 °F
0.0000675 ohm-cm

@Temperature 100 °C
 0.0000675 ohm-cm

@Temperature 212 °F
0.0000770 ohm-cm

@Temperature 200 °C
 0.0000770 ohm-cm

@Temperature 392 °F
0.0000925 ohm-cm

@Temperature 400 °C
 0.0000925 ohm-cm

@Temperature 752 °F
0.000105 ohm-cm

@Temperature 600 °C
 0.000105 ohm-cm

@Temperature 1110 °F
0.000115 ohm-cm

@Temperature 800 °C
 0.000115 ohm-cm

@Temperature 1470 °F