Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 11.9 µm/m-°C @Temperature 0.000 - 100 °C |
6.61 µin/in-°F @Temperature 32.0 - 212 °F |
|
Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 300 °C |
6.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
International Mold Steel Daido DRM3 Matrix High-Speed Steel This conventional grade MH88 has been improved to DRM3. High hardness and tough DRM3 with excellent hardenability is suitable for high precision cold working tools.Information provided by Internatio.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 300 °C |
6.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 30.0 - 100 °C |
6.60 µin/in-°F @Temperature 86.0 - 212 °F |
|
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure – no pin holes, inclusions or hard spots. 30-3.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 100 °C |
6.61 µin/in-°F @Temperature 68.0 - 212 °F |
|
Latrobe LSSâ„¢ 2367 Hot Work Tool Steel TLS 2367 is a chromium-molybdenum hot work steel that is similar to AISI H11 hot work steel, but which contains a higher molybdenum content. The higher molybdenum gives TLS 2367 better hot hardness .. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 200 °C |
6.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
Schmolz + Bickenbach Thermodur® 2999 Hot Work Die Steel Description: Maximum high-temperature strength, good high-temperature wear resistance, excellent thermal shock resistance and thermal conductivity across the entire range of service temperatures App.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 788 °C |
6.60 µin/in-°F @Temperature 68.0 - 1450 °F |
|
Crucible Steel 430F Stainless Steel Crucible 430F is a low carbon, high chromium ferritic stainless steel, specially developed for solenoid core applications in corrosive environments. The chemistry is closely controlled to develop o.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 21.1 - 427 °C |
6.60 µin/in-°F @Temperature 70.0 - 800 °F |
|
Crucible Steel REX® M3-1 High Speed Steel, AISI M3-1 REX M3-1 is a lower carbon, lower vanadium modification of M3-2 high speed steel. This lower alloy content results in better machining and grinding characteristics compared to M3-2, with a slight im.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 300 °C |
6.61 µin/in-°F @Temperature 572 °F |
|
Bohler-Uddeholm BÖHLER S401(M1) High Speed Steel Description: Molybdenum high speed steel with high toughness and good cutting ability. Applications: Taps, twist drills, reamers, milling tools, broaches toolsStandards: DIN/EN 1.3346 HS2-91, AISI M.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 787 °C |
6.61 µin/in-°F @Temperature 68.0 - 1450 °F |
|
ATI Allegheny Ludlum AL 403™ Martensitic Stainless Steel Characteristics: corrosion resistant, heat resistant, oxidation resistant up to 1400°F.Information provided by Allegheny Ludlum |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150 (Heated 621°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature <=427 °C |
6.61 µin/in-°F @Temperature <=801 °F |
|
AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition TH 1050 AK Steel 17-7 PH® provides high strength and hardness, excellent fatigue properties, good corrosion resistance, good formability, and minimum distortion upon heat treatment. This alloy provides va.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |