Polymer Property : Electrical Resistivity = 0.000105 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Electrical Properties Metric English Comments
Electrical Resistivity 0.000105 ohm-cm

@Temperature 93.0 °C
0.000105 ohm-cm

@Temperature 199 °F
H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy
MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 1.6 mm sheet
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 12.7-50.8 mm bar
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, 6.3-38.1 mm plate
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 316°C
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, aged 1000 hours at 982°C
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, all-weld metal, GTAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, all-weld metal, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, mill annealed
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, plate, GMAW weld (short)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
Haynes Ultimet® alloy, plate, GMAW weld (spray)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Electrical Resistivity 0.000105 ohm-cm

@Temperature 600 °C
0.000105 ohm-cm

@Temperature 1110 °F
ATI Allegheny Ludlum 430 Ferritic Stainless Steel
Characteristics:oxidation resistant at elevated temperatures, corrosion resistance approaching nickel-bearing stainless steels in mildly corrosive environments, ductile, does not work harden readily..