Polymer Property : Tensile Strength, Ultimate = 483 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	483 MPa @Thickness 9.50 mm, Temperature 760 Â°C	70100 psi @Thickness 0.374 in, Temperature 1400 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	483 MPa @Temperature 649 Â°C	70100 psi @Temperature 1200 Â°F
Haynes HastelloyÂ® G-35Â® Nickel Alloy Plate, Annealed at 2075Â°F (1135Â°C) Known for its corrosion performance, HASTELLOYÂ® G-35Â® alloy was designed to resist â€œwet processâ€ phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate	483 - 545 MPa @Thickness 0.508 - 1.52 mm	70100 - 79000 psi @Thickness 0.0200 - 0.0600 in
ATI Allegheny Ludlum 430 Ferritic Stainless Steel Characteristics:oxidation resistant at elevated temperatures, corrosion resistance approaching nickel-bearing stainless steels in mildly corrosive environments, ductile, does not work harden readily..
Tensile Strength, Ultimate	483 MPa @Temperature 760 °C	70100 psi @Temperature 1400 °F
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed..
Tensile Strength, Ultimate	483 MPa @Temperature 649 °C	70100 psi @Temperature 1200 °F
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..