Advanced Polymer Alloys Alcryn® 4660 NC Melt Processable Rubber

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer APA - Advanced Polymer Alloys
Trade Name Alcryn®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Polymer Alloys Alcryn® 4660 NC Melt Processable Rubber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high productivity on thermoplastic processing equipment.Applications:Window and door weatherstripping (and other complex profile extrusions)Soft handles and gripsMolded seals and gasketsInjection-molded and co-injection molded partsBlow-molded partsTubing and hoseWire and cable jacketsCoated fabrics and sheet goodsInformation provided by Advanced Polymer Alloys
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D471; ISO 2781
Viscosity 400000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
400000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
ASTM D3835
Mechanical Properties Metric English Comments
Hardness, Shore A 54
54
After 7 days at 257°F (125°C); ASTM D573; ISO 188
57
57
ASTM D2240; ISO 48
Tensile Strength, Ultimate 8.27 MPa
1200 psi
After 7 days at 257°F (125°C); ASTM D573; ISO 188
8.446 MPa
1225 psi
ASTM D412; ISO 37
Elongation at Break 400 %
400 %
After 7 days at 257°F (125°C); ASTM D573; ISO 188
440 %
440 %
ASTM D412; ISO 37
100% Modulus 0.00255 GPa
0.370 ksi
After 7 days at 257°F (125°C); ASTM D573; ISO 188
0.00262 GPa
0.380 ksi
ASTM D412; ISO 37
Graves Tear Strength 29.8 kN/m

@Temperature 23.9 °C
170 pli

@Temperature 75.0 °F
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 4.0
4.0
Cs-17 Wheel, 1000 g Load; ASTM D3389
Compression Set 16 %
16 %
After 22 Hr at 75°F (24°C); ASTM D395; ISO 815
72 %

@Temperature 100 °C
72 %

@Temperature 212 °F
22 hrs.; ASTM D395; ISO 815
Tensile Set 7.0 %
7.0 %
ASTM D412
Torsional Stiffness 1.7225 MPa
249.83 psi
At 75°F (24°C); ASTM D1043
6.89 MPa
999 psi
At -4°F (-20°C); ASTM D1043
Thermal Properties Metric English Comments
Brittleness Temperature -68.9 °C
-92.0 °F
ASTM D746; ISO 812
Clash Berg Stiffness Temperature -40.0 °C
-40.0 °F
At 10,000 psi (69 Mpa); ASTM D1043
Processing Properties Metric English Comments
Processing Temperature 166 °C
330 °F
Descriptive Properties Value Comments
Fluid Resistance - Volume Change, % (ASTM D471) 13
After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)
14
After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)
-19
After 7 Days in ASTM Oil No.1 at 212°F (100°C)
9
After 7 Days in Water at 212°F (100°C)