Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 9.00 - 13.0 MPa | 1310 - 1890 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 8502 BLK The fogging test value is 90% according to ASTM SAE-J275. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Multibase Multi-Flex® TPE A 8502 LC BLK Multi-Flex® LC compounds are a new generation elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Shell's Kraton G technology and featur.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 8802 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 9103 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Multibase Multi-Flex® TPE G 7821 Multi-Flex® high heat compounds are a new generations elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Kraton G technology and featur.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6509 Multi-Flex® A-6509 thermoplastic elastomer blend is designed to provide processors with cost effective compounds with excellent tear strength, tensile strength and high elongation. Multi-Flex® A-.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | |
Reliance Industries METABOLIX PHO Information provided by Reliance Industries |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1390P Polyethylene
(discontinued **) Low-density polyethylene 1390P is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density polyethylen.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 811A Polyethylene
(discontinued **) Injection grade. With its high melt index, the material flows well in molding machines and fills large molds with ease. It is used for molding housewares and other items where a flexible, easy mol.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE5082 Extrusion Coating Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings (sugar paper and laminations).FDA Notes: Con.. |
|||
Tensile Strength, Ultimate | 9.00 - 80.0 MPa | 1310 - 11600 psi | Average value: 30.1 MPa Grade Count:177 |
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 9.00 - 161.337 MPa @Temperature -40.0 - 120 °C |
1310 - 23400.0 psi @Temperature -40.0 - 248 °F |
Average value: 69.4 MPa Grade Count:3 |
Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
DuPont Performance Polymers Kalrez® 1058 FFKM Perfluoroelastomer
(discontinued **) A carbon black-filled compound that has been plasticized with perfluorinated oil. It is the softest, lowest modulus compound in the Kalrez line. Generally it is similar in resistance to Compound 1.. |
|||
Tensile Strength, Ultimate | 9.02 MPa @Treatment Temp. 150 °C, Time 605000 sec |
1310 psi @Treatment Temp. 302 °F, Time 168 hour |
Heat Aging; ASTM D 412/ASTM D 573 |
Zylog Neoplast® 173 FT EB Thermoplastic Vulcanizate Neoplast 173 FT EB is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding, Blow Molding and Extrusion applications.Ro.. |
|||
Tensile Strength, Ultimate | 9.00 MPa @Temperature 49.0 °C |
1310 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | |
ATG s.r.l. EACM Ethylene-Acrylic Rubber |
|||
Tensile Strength, Ultimate | 9.03 MPa | 1310 psi | ASTM D412; ISO 37 |
Advanced Polymer Alloys Alcryn® 4670 BK Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 9.03 MPa | 1310 psi | silicone property; ASTM D412 |
Arlon 49283R040 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil polyethylene; Side 1: cured silicone rubber; Substrate: 1681 Fiberglass; Side 2: cured silicone rubber |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2035 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Medium flow resin with good stiffness.Applications: Injection molding: color concentrates.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under c.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2051 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very good molding processability, produces parts with good stiffness, and shows excellent flatness in large projected areas. Also recommended for multi-cavit.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2060 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High flow characteristics, good processability.Applications: Injection molding: general purpose molding, large moldings including housewares and toys.FDA Note.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2072 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, gloss, and stiffness.Applications: Injection molding: lids and difficult to fill applications... |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2075 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: .. |
|||
Tensile Strength, Ultimate | 9.00 - 25.0 MPa | 1310 - 3630 psi | Average value: 13.0 MPa Grade Count:20 |
Overview of materials for Low Density Polyethylene (LDPE), Wire/Cable Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Wire/Cable Grade". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 9.00 - 62.0 MPa | 1310 - 8990 psi | Average value: 41.4 MPa Grade Count:56 |
Overview of materials for Polyether Block Amide (PEBA) This property data is a summary of similar materials in the MatWeb database for the category "Polyether Block Amide (PEBA)". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 9.00 - 50.9 MPa | 1310 - 7380 psi | Average value: 34.0 MPa Grade Count:3 |
Overview of materials for ABS/PVC Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Tensile Strength, Ultimate | 9.00 - 60.0 MPa @Temperature 60.0 - 120 °C |
1310 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |
|||
Tensile Strength, Ultimate | 9.00 - 80.0 MPa @Temperature 60.0 - 120 °C |
1310 - 11600 psi @Temperature 140 - 248 °F |
Average value: 31.0 MPa Grade Count:2 |
Overview of materials for Polypropylene, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum .. |