Eastman 1390P Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman 1390P Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low-density polyethylene 1390P is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density polyethylene coating materials that have considerably lower melt indexes, 1390P has slightly better adhesion to paper substrates and can be heat-sealed at a slightly lower temperature. However, high melt index coating materials produce slightly more neck-in and a narrower heat-sealing temperature range. Designed for applications such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combination of high melt index and low density also provides good heat seals at high packaging or sealing rates.List of Applications:Coatings for paper/paperboardInformation supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.915 g/cc
0.0331 lb/in³
ASTM D4883
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 9.00 MPa
1310 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Tensile Strength, Yield 10.0 MPa
1450 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Elongation at Break 300 %
300 %
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Flexural Modulus 0.193 GPa
28.0 ksi
2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790
Thermal Properties Metric English Comments
Vicat Softening Point 86.0 °C
187 °F
ASTM D1525
Brittleness Temperature -52.0 °C
-61.6 °F
ASTM D746
Descriptive Properties Value Comments
Process Coating