Huntsman PE5082 Extrusion Coating Polyethylene (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman PE5082 Extrusion Coating Polyethylene (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings (sugar paper and laminations).FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.916 g/cc	0.0331 lb/in³	ASTM D1505
Melt Flow	14 g/10 min	14 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	42	42	ASTM D2240
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D638
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	220 %	220 %	ASTM D882
Elongation at Break	600 %	600 %	ASTM D638
Modulus of Elasticity	0.152 GPa	22.0 ksi	Secant; ASTM D638
Secant Modulus, MD	0.0830 GPa	12.0 ksi	ASTM D882
Secant Modulus, TD	0.124 GPa	18.0 ksi	ASTM D882
Film Tensile Strength at Break, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Break, TD	10.0 MPa	1450 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	85.0 °C	185 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	249 - 288 °C	480 - 550 °F