SABIC Innovative Plastics LNP Thermocomp 2C003

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp 2C003.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* 2C003 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ASTM D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ASTM D 638
90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 4.9 %
4.9 %
ASTM D 638
4.9 %
4.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 11.71 GPa
1698 ksi
50 mm/min; ASTM D 638
Flexural Strength 137 MPa
19900 psi
ASTM D 790
137 MPa
19900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 11.03 GPa
1600 ksi
ASTM D 790
11.03 GPa
1600 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 3.52 J/cm

@Temperature 23.0 °C
6.59 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 12.38 J/cm

@Temperature 23.0 °C
23.19 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648