Wellman Wellamid® GSF25/15-66 22L-N 40% Glass Sphere/Fiber Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GSF25/15-66 22L-N 40% Glass Sphere/Fiber Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Sphere/Fiber Reinforced Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183-87 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-93 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-93 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178-93 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Middle Barrel Temperature | 271 - 288 °C | 520 - 550 °F | |
| Front Barrel Temperature | 260 - 277 °C | 500 - 530 °F | |
| Nozzle Temperature | 260 - 288 °C | 500 - 550 °F | |
| Melt Temperature | 277 - 304 °C | 530 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6840 PC+ABS (Europe-Africa-Middle East)
- NOVA Chemicals Sclair® 69A HDPE Extrusion Resin (discontinued **)
- Lord Adhesives Thermosetâ„¢ MD-200 Electrically Conductive Die-Attach Adhesive
- Micropol Microlin ML91 Linear Polyethylene Rotational Molding Powder
- SABIC Innovative Plastics LNP Stat-kon EE005 PEI (Asia Pacific)
- SABIC Innovative Plastics Xenoy® IQ1103U PBT+PC (Asia Pacific)
- Teknor Apex Chemlon® 225-15 MG Nylon 6, 25% Mineral Reinforced, 15% Glass Fiber Reinforced
- DSM Akulon® S223-G6 Nylon 66-30% Glass Reinforced (European and Asian Grade) (Dry)
- Braskem LH118 Linear Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved