Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 33 g/10 min @Load 10.0 kg, Temperature 250 °C |
33 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 63.7 MPa | 9240 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 84.3 MPa | 12200 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 5.2 % | 5.2 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.24 GPa | 469 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 4.02 GPa | 583 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 6.35 mm |
0.918 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.549 J/cm @Thickness 3.17 mm |
1.03 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 143 °C | 289 °F | B/50; ISO R306 |
| 145 °C | 293 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 - 1.60 mm |
V-0 @Thickness 0.0591 - 0.0630 in |
Users viewing this material also viewed the following:
- Pyrotek NT-C Electrical Insulating Material
- Ferro IP 780 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- LG Chemical Lupoy 1603-06 Polycarbonate Resin
- Techmer ES Elastoblend® PA6 IM 835 HS L
- Teknor Apex APEX® 1700-70 Polyvinyl Chloride, Flexible
- Unipetrol PE HD LITEN® MB/ML 87 HDPE
- A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Daikin NEOFLON NC-1539 FEP Coating Powder, Gray
- DuPont Teijin Films Teijin® Tetoron® HS Polyester Film, 1000 Gauge
- 3M FM033 Indoor UL Recognized Clear Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved