SABIC Innovative Plastics LNP THERMOCOMP DF006RXQ PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF006RXQ PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DF006RXQ is a compound based on Polycarbonate resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| 1.424 g/cc | 0.05145 lb/in³ | ASTM D792 | |
| Water Absorption | 0.16 % @Time 86400 sec |
0.16 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| 3.4 % | 3.4 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.88 GPa | 998 ksi | 1 mm/min; ISO 527 |
| 7.71 GPa | 1120 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 179 MPa | 26000 psi | 2 mm/min; ISO 178 |
| 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 179 MPa | 26000 psi | 2 mm/min; ISO 178 |
| 187 MPa | 27100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.37 GPa | 1070 ksi | 2 mm/min; ISO 178 |
| 7.66 GPa | 1110 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.48 J/cm | 2.77 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.30 J/cm | 17.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J | 16.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 51.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Latrobe Lescalloy® AF 1410 VIM-VAR ; 9 in High Strength Alloy Steel
- Menzolit Menzolit® BMC 2910 Unsaturated Polyester UP
- Silberline Tufflake® 3700
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Covestro Apec® HT KU 1-9361 High-Heat Polycarbonate
- Bohler-Uddeholm UDDEHOLM HOTVAR® Hot Work Tool Steel
- Axiall 83-126J Moldings & Extrusions Flexible PVC
- Arkema Group LOTRYL® 17 BA 07 Copolymer Ethylene - Butyl Acrylate
Copyright © lookpolymers.com All Rights Reserved