Wellman EcoLon® MRGF1616-BK 40% Mineral/Glass Reinforced Post Consumer Compound Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | EcoLon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman EcoLon® MRGF1616-BK 40% Mineral/Glass Reinforced Post Consumer Compound Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Mineral/Glass Reinforced Post Consumer Compound Nylon 6Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183-87 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-93 |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-93 |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178-93 |
| Flexural Modulus | 9.35 GPa | 1360 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 5.60 kJ/m² | 2.66 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 277 - 293 °C | 530 - 560 °F | |
| Middle Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Front Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Nozzle Temperature | 254 - 282 °C | 490 - 540 °F | |
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® 1000 LSG PEEK, Biocompatibility tested (ISO Product Data Sheet)
- Plastcom SLOVAMID 6/66 CF 30 PA6/66, 30% carbon fibre
- LG Chemical LUCEL N145-02 General Purpose POM, Unreinforced, Externally Lubricated, Ultra High Flow
- SABIC Innovative Plastics ULTEM 2310 PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP DF008 PC
- A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
- Fainplast Compounds PM 5525 Flexible PVC, Lead Free
- Caplinq LINQSTAT™ VCF-40036S/2
- BASF Ultramid® B32 0.015 BOPA Film
Copyright © lookpolymers.com All Rights Reserved