Teknor Apex Chemlon® 212 Nylon 6, Unreinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Teknor Apex Company
Trade Name Chemlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Chemlon® 212 Nylon 6, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Lubricated, General Purpose; General purpose nylon 6; Slightly tougher and more ductile than nylon 66 Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Linear Mold Shrinkage 0.014 - 0.018 cm/cm
0.014 - 0.018 in/in
ASTM D955
Melt Flow 8.00 g/10 min

@Load 1.00 kg,
Temperature 235 °C
 8.00 g/10 min

@Load 2.20 lb,
Temperature 455 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength 79.3 MPa
11500 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ASTM D638
Flexural Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 2.86 GPa
415 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
 1.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 61.2 µm/m-°C
34.0 µin/in-°F
ASTM D696
Melting Point 216 °C
420 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 92.2 °C
198 °F
Unannealed; ASTM D648
UL RTI, Electrical 125 °C

@Thickness 0.810 mm
 257 °F

@Thickness 0.0319 in
 UL 746
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0590 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.810 mm
 167 °F

@Thickness 0.0319 in
 UL 746
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0590 in
 UL 746
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 110 °C

@Thickness 0.810 mm
 230 °F

@Thickness 0.0319 in
 UL 746
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0590 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-2

@Thickness 0.810 mm
 V-2

@Thickness 0.0319 in
Oxygen Index 25 %
25 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 14.2 kV/mm

@Thickness 3.00 mm
 360 kV/in

@Thickness 0.118 in
 ASTM D149
Comparative Tracking Index 600 V
600 V
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 218 - 235 °C
425 - 455 °F
Middle Barrel Temperature 229 - 252 °C
445 - 485 °F
Front Barrel Temperature 241 - 260 °C
465 - 500 °F
Nozzle Temperature 241 - 266 °C
465 - 510 °F
Melt Temperature 241 - 266 °C
465 - 510 °F
Processing Temperature
Drying Temperature 79.4 °C
175 °F
Descriptive Properties Value Comments
Suggested Moisture, max 0.2
Suggested Regrind, max 25