ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A low gel 29.5% vinyl acetate copolymer designed for film and compounding applications. The resin provides very low modulus films with high tensile strength.Applications: Low modulus films; Elastic films; Compounding.

Physical Properties	Metric	English	Comments
Density	0.952 g/cc	0.0344 lb/in³	Exxon Method
Environmental Stress Crack Resistance	>= 500 hour	>= 500 hour	F50, Condition A; ASTM D1693
Melt Flow	3.1 g/10 min	3.1 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	72	72	ASTM D2240
Hardness, Shore D	23	23	ASTM D2240
Tensile Strength, Ultimate	14.0 MPa	2030 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0190 GPa	2.76 ksi	1% Secant, ASTM D790
Tensile Impact Strength	815 kJ/m²	388 ft-lb/in²	23°C; ASTM D-1822

Thermal Properties	Metric	English	Comments
Melting Point	70.0 °C	158 °F	Exxon Method
Vicat Softening Point	48.0 °C	118 °F	1000g; ASTM D-1525