Niche Polymer PCABSN10BK PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced |
| Manufacturer | Niche Polymer |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Niche Polymer PCABSN10BK PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Niche Polymer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.00600 cm/cm | 0.00600 in/in | ASTM D955 |
| Melt Flow | 10.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
10.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D123 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 6.00 % | 6.00 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Unnotched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D789 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 30 Ethylene Vinyl Acetate Copolymer - Injection Molding & Profile Extrusion
- Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled
- Karina E 822-10/148-CRB-LMP White PVC Compound
- Teknor Apex Uniprene® UN-7010-64NT Thermoplastic Vulcanizate
- Von Roll Isola IMI Varnish 701 Solventless Polyester Varnish for Electrical Insulation
- A. Schulman POLYBATCH™ Blue LL40434 Concentrate Based In LLDPE
- Total PS CPDS 818E Flame Retardant Polystyrene
- A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
- Arlon LW601Xxx-P1 0.060" (1.52 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Alliance S-26A Samarium Cobalt Magnetic Material
Copyright © lookpolymers.com All Rights Reserved