Styrolution LuranÂ® S 757 G Q43 White 36609 ASA

Category	Polymer , Thermoplastic , ASA Polymer
Manufacturer	Styrolution
Trade Name	Luran®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution LuranÂ® S 757 G Q43 White 36609 ASA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Particularly easy flowing injection molding grade for difficult moldings with large flow path/wall thickness ratios.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/inÂ³	ISO 1183
Water Absorption	1.65 %	1.65 %	Equilibrium; ISO 62
	0.45 % @Time 86400 sec	0.45 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	0.35 %	0.35 %	23Â°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Melt Flow	26.75 g/10 min @Load 10.0 kg, Temperature 220 Â°C	26.75 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	90.0 MPa @Load 36.5 kg, Time 30.0 sec	13100 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	51.0 MPa	7400 psi	50 mm/min; ISO 527-1/-2
Elongation at Break	8.0 %	8.0 %	Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield	3.3 %	3.3 %	50 mm/min; ISO 527-1/-2
Tensile Modulus	2.40 GPa	348 ksi	ISO 527-1/-2
Flexural Strength	75.0 MPa	10900 psi	ISO 178
Poissons Ratio	0.33	0.33	Calculated
Shear Modulus	0.900 GPa	131 ksi	ISO 6721-2
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ASTM D256
Charpy Impact Unnotched	8.00 J/cmÂ² @Temperature -30.0 Â°C	38.1 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	19.0 J/cmÂ² @Temperature 23.0 Â°C	90.4 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
Charpy Impact, Notched	0.300 J/cmÂ² @Temperature -30.0 Â°C	1.43 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	1.20 J/cmÂ² @Temperature 23.0 Â°C	5.71 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	1650 MPa @Strain <=0.500 %	239000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 - 110 Âµm/m-Â°C @Temperature 23.0 - 80.0 Â°C	44.4 - 61.1 Âµin/in-Â°F @Temperature 73.4 - 176 Â°F	ISO 11359-1/-2
Thermal Conductivity	0.170 W/m-K	1.18 BTU-in/hr-ftÂ²-Â°F	DIN 52612-1
Maximum Service Temperature, Air	85.0 Â°C	185 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	101 Â°C	214 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	96.0 Â°C	205 Â°F	ISO 75-1/-2
Vicat Softening Point	97.0 Â°C	207 Â°F	VST/B/50; ISO 306
	105 Â°C	221 Â°F	VST/A/50; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Diameter 4.00 mm	HB @Diameter 0.157 in	IEC 60707

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 100 Hz	3.4 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm	889 kV/in	K20/P20; IEC 60243-1
Dissipation Factor	0.010 @Frequency 100 Hz	0.010 @Frequency 100 Hz	IEC 60250
	0.025 @Frequency 1.00e+6 Hz	0.025 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Liquid A; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	240 - 280 Â°C	464 - 536 Â°F	Injection
Mold Temperature	40.0 - 80.0 Â°C	104 - 176 Â°F	Injection
Drying Temperature	80.0 Â°C	176 Â°F	Pre-drying
Dry Time	2 - 4 hour	2 - 4 hour	Pre-drying

Descriptive Properties	Value	Comments
Color	White 36609
Commercial Status	Europe
Primary Processing Technique	Injection Molding