- Lucent Polymers TPP-130 Polypropylene, Homopolymer, 30% Talc Filled
Lucent Polymers TPP-130 Polypropylene, Homopolymer, 30% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPP-130 Polypropylene, Homopolymer, 30% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.72 MPa | 4601 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 52.41 MPa | 7601 psi | ASTM D790 |
| Flexural Modulus | 3.034 GPa | 440.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.44 °C | 175.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-216-P(HT) Powdered Metal
- H.C. Starck Grade K2 Crystalline Boron
- Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F)
- Shuman 210 Polyphenylene Ether Copolymer Alloy
- Cossa Polimeri ESTASTIR HI 0508 V0 Flame Retardant Polystyrene
- PolyOne Synprene® IT 38-034M Thermoplastic Elastomer - SBC (discontinued **)
- Henkel Hysol EA 9396/C-2 Paste Adhesive System
- LyondellBasell Pro-fax SV152 Polypropylene Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved