Star Plastics ABSGF30 Molding Grade ABS With 30% Glass

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
Manufacturer Star Plastics, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics ABSGF30 Molding Grade ABS With 30% Glass.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Maximum Moisture Content 0.15
0.15
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Melt Flow 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.5 MPa
9500 psi
ASTM D638
Tensile Modulus 5.86 GPa
850 ksi
ASTM D638
Flexural Yield Strength 98.6 MPa
14300 psi
ASTM D790
Flexural Modulus 6.83 GPa
990 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm
1.00 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
215 °F
unannealed, .125in; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 188 - 218 °C
370 - 425 °F
Middle Barrel Temperature 204 - 232 °C
400 - 450 °F
Front Barrel Temperature 218 - 246 °C
425 - 475 °F
Nozzle Temperature 218 - 274 °C
425 - 525 °F
Melt Temperature 218 - 274 °C
425 - 525 °F
Mold Temperature 48.9 - 76.7 °C
120 - 170 °F
Drying Temperature 82.2 - 93.3 °C
180 - 200 °F
Dry Time 2 - 4 hour
2 - 4 hour
Back Pressure 0.172 - 0.689 MPa
25.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm