PolyOne Geon™ Vinyl Rigid Extrusion 87707 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87707 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.87 GPa | 416 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 93.5 MPa | 13600 psi | ASTM D790 |
| Flexural Modulus | 2.92 GPa | 424 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.300 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 0.210 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.393 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| 0.350 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.656 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 66.3 J/cm @Temperature 23.0 °C |
0.124 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 175 J/cm @Temperature 23.0 °C |
0.328 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | General Purpose | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 11553 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® CH G0 Very Low Density Polyethylene
- SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS
- SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Europe-Africa-Middle East)
- A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene
- Hexcel® HexForce™ 1680 Fiber Glass Fabric
- ExxonMobil Bicor™ 32MB768 OPP Film
- Colorite Polymers Weatherflex™ CS1534WX (NTL01P) Wire and Cable Vinyl Compound
- 3M Jet-Weld™ TE-100 Adhesive
- Aptek 2100-A/B Urethane Encapsulant and/or Potting Compound
Copyright © lookpolymers.com All Rights Reserved