Solvay TECHNYL® SSD 330 KNF/E PA66, 15% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® SSD 330 KNF/E PA66, 15% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 33% of glass fiber, for injection molding specially stabilized to improves its resistance to automotive cooling liquids.Available in: Asia PacificProduct Applications: TECHNYL® SSD 330 KNF/E is particularly recommended for the injection molding of parts in permanent contact with cooling liquids in cars, such as: cooling and heating radiator systems, header tanks, thermostat components, and inlet/outlet pipes. This product is available in Black and in color on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183/A |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D786 |
| Tensile Strength, Yield | 195 MPa | 28300 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 300 MPa | 43500 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
12.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 262 °C | 504 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
| Flammability, UL94 | HB | HB | 1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS (Europe-Africa-Middle East)
- H.C. Starck HPM 1801 Tungsten High Density Composite
- Polyram Polytron P50B11 Homopolymer Polypropylene, Chemically Coupled 50% LGF
- Covestro Bayflex® XGT-140 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Ensinger Tecatron® XP-71 Compression Molded PPS Compound, 20% PTFE Filled Natural
- Azoty Tarnow™ Tarnamid® T-27 MW30 Polyamide 6 - Mineral Reinforced
- Lubrizol ESTANE® T5191 Ether Based Thermoplastic Polyurethane (European Grade)
- SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved