- Solvay TECHNYL® A 30 H1 V25 PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 30 H1 V25 PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 30 H1 V25 PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame-retardant polyamide 66, 25% glass-fiber reinforced, heat stabilized for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This flame retardant material, U.L. 94 V0 rated at 0.8 mm, shows high Glow-wire, CTI values and good mechanical properties .It can be supplied in various colors. This grade is suitable for molding insulating parts for electrical devices: switches, rotary switches, timers and contactors. This product is available in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 Type 1A |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 Type 1A |
| Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527 Type 1A |
| Izod Impact, Notched (ISO) | 9.80 kJ/m² | 4.66 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
1210 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
1210 | |
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
1210 | |
| Glow Wire Test | 960 °C | 1760 °F | ISO 60695-2-12 |
| 960 °C | 1760 °F | ISO 60695-2-12 | |
| 775 °C @Thickness 0.800 mm |
1430 °F @Thickness 0.0315 in |
ignition temperature; ISO 60695-2-13 | |
| 775 °C @Thickness 1.60 mm |
1430 °F @Thickness 0.0630 in |
ignition temperature; ISO 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 275 - 280 °C | 527 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 280-285°C |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3740 TPE, PP Overmold or Standalone use
- Michelman® ACqua™ 240 Anionic Polyethylene Emulsion
- Techmer ES HiFill® PA6/6 CM40 6122 BK 40% Mineral Filled
- Saint-Gobain Chemfab® TCK® 800 High-Strength Leno Weave Small Open Mesh Belting Material
- Silikony Polskie Polsil Gum 100/50 HTV Silicone Rubber
- Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, Aramid Balanced fabric 175 g/m2
- DuPont™ Bynel® 41E850 Anhydride Modified LLDPE
- Diamond Polymers ABS 3003MC Black 1722
- BASF Paliotan® Yellow L 1645 Color Additive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N774 (SRF) Filler
Copyright © lookpolymers.com All Rights Reserved