PolyOne Maxxam™ PPH-20C Nat Polypropylene Homopolymer (PP Homopolymer)

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	PolyOne Corporation
Trade Name	Maxxam™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Maxxam™ PPH-20C Nat Polypropylene Homopolymer (PP Homopolymer).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	ASTM D955
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 230 °C	11 g/10 min @Load 4.76 lb, Temperature 446 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	90	90	ASTM D785
Tensile Strength, Yield	30.0 MPa	4350 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	99 %	99 %	Type I, 51 mm/min; ASTM D638
Flexural Strength	35.9 MPa	5210 psi	ASTM D790
Flexural Modulus	1.93 GPa	280 ksi	ASTM D790
Izod Impact, Notched	0.370 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.693 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Unnotched	4.50 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	8.43 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C @Thickness 3.18 mm	210 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	ALL; UL 94

Processing Properties	Metric	English	Comments
Mold Temperature	16.0 - 50.0 °C	60.8 - 122 °F

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	General Purpose
	Homopolymer
Filler / Reinforcement	Calcium Carbonate Filler
	Unspecified FillerReinfor., 20% Filler by Weight
Forms	Pellets
Generic Material	PP Homopolymer
Generic Name	Polypropylene Homopolymer (PP Homopolymer)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications