PolyOne Versalloy™ HC 9210-45N Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versalloy™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versalloy™ HC 9210-45N Thermoplastic Elastomer (TPE).pdf
  Online Service   lookpolymers   27660005
Material Notes:
Versalloy™ HC 9210-45N is a USP Class VI, TPV alloy targeted for injection molding healthcare applications such as disposable medical items, syringe stoppers, and soft-touch overmolding onto surgical grips. Product exhibits exceptional flow properties and surface aesthetics. * Excellent Flow for Long, Thin Flow Paths * Exceptional Colorability * Overmold Adhesion to Polypropylene * Superior Surface Aesthetics * USP Class VIVersalloy™ HC 9210-45N can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times. Municipality waste stream recycle code is 7 which is designated for Other. Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.Color concentrates with polypropylene (PP) carrier are most suitable for coloring Versalloy™ HC 9210-45N. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versalloy™ HC 9210-45N with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versalloy™ HC 9210-45N has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 5 in/sec 1st Stage - Boost Pressure: 300 to 700 psi 2nd Stage - Hold Pressure: 70% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.888 g/cc
0.888 g/cc
Viscosity 116 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
116 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Mechanical Properties Metric English Comments
Hardness, Shore A 45
10 sec; ASTM D2240
Tensile Strength at Break 3.34 MPa

@Temperature 23.0 °C
484 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.10 MPa

@Strain 100 %,
Temperature 21.0 °C
160 psi

@Strain 100 %,
Temperature 69.8 °F
Die C2 hr; ASTM D412
2.21 MPa

@Strain 300 %,
Temperature 23.0 °C
321 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 480 %

@Temperature 23.0 °C
480 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 17.5 kN/m

@Temperature 21.0 °C
99.9 pli

@Temperature 69.8 °F
Die C2 hr; ASTM D624
Compression Set 19 %

@Temperature 23.0 °C,
Time 79200 sec
19 %

@Temperature 73.4 °F,
Time 22.0 hour
34 %

@Temperature 70.0 °C,
Time 79200 sec
34 %

@Temperature 158 °F,
Time 22.0 hour
39 %

@Temperature 100 °C,
Time 79200 sec
39 %

@Temperature 212 °F,
Time 22.0 hour
Processing Properties Metric English Comments
Rear Barrel Temperature 149 - 188 °C
300 - 370 °F
Middle Barrel Temperature 160 - 199 °C
320 - 390 °F
Front Barrel Temperature 171 - 210 °C
340 - 410 °F
Nozzle Temperature 171 - 210 °C
340 - 410 °F
Mold Temperature 15.6 - 26.7 °C
60.1 - 80.1 °F
Back Pressure 0.689 - 1.38 MPa
99.9 - 200 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Agency Ratings USP Class VI
Appearance Natural Color
Features Good Colorability
Good Processability
Good Surface Finish
Halogen Free
High Flow
Non-Phthalate Plasticizer
Recyclable Material
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Flexible Grips
Medical/Healthcare Applications
Personal Care
Soft Touch Applications
Thin-walled Parts