Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a broad temperature range. It also displays low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel HFZ A-4133 L resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. - Black: HFZ A-4133 L BK 324 - Natural: HFZ A-4133 L NTInjection Notes: Injection Pressure: 3 to 4 in/secInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.46 g/cc	0.0527 lb/in³	ISO 1183/A
Filler Content	33 %	33 %	Glass Fiber Reinforcement
Water Absorption	0.26 % @Time 86400 sec	0.26 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	180 MPa	26100 psi	ISO 527-2
Elongation at Break	1.8 %	1.8 %	ISO 527-2
Tensile Modulus	12.0 GPa	1740 ksi	ISO 527-2
Flexural Strength	255 MPa	37000 psi	ISO 178
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Izod Impact, Notched (ISO)	8.40 kJ/m²	4.00 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	40.0 kJ/m²	19.0 ft-lb/in²	ISO 180/1U
Charpy Impact, Notched	0.820 J/cm²	3.90 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	14.0 µm/m-°C @Temperature 150 - 250 °C	7.78 µin/in-°F @Temperature 302 - 482 °F	TMA; ASTM E831
	20.0 µm/m-°C @Temperature 0.000 - 90.0 °C	11.1 µin/in-°F @Temperature 32.0 - 194 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	63.0 µm/m-°C @Temperature 0.000 - 90.0 °C	35.0 µin/in-°F @Temperature 32.0 - 194 °F	ASTM E831
	150 µm/m-°C @Temperature 150 - 250 °C	83.3 µin/in-°F @Temperature 302 - 482 °F	ASTM E831
Melting Point	327 °C	621 °F	ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	Unannealed; ISO 75-2/A
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	UL 94
Glow Wire Test	800 °C	1470 °F	Glow Wire Flammability Index; IEC 60695-2-12
	800 °C	1470 °F	Glow Wire Ignition Temperature; IEC 60695-2-13

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	ASTM D150
	3.9 @Frequency 60.0 Hz	3.9 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	19.0 kV/mm	483 kV/in	ASTM D149
Dissipation Factor	0.0060 @Frequency 60.0 Hz	0.0060 @Frequency 60.0 Hz	ASTM D150
	0.016 @Frequency 1.00e+6 Hz	0.016 @Frequency 1.00e+6 Hz	ASTM D150
High Voltage Arc Resistance to Ignition (HVAR)	>= 300 sec	>= 300 sec	PLC 0; UL 746
Hot Wire Ignition, HWI	60 - 120 sec	60 - 120 sec	PLC 1; UL 746
High Amp Arc Ignition, HAI	>= 120 arcs	>= 120 arcs	PLC 0; UL 746
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min	0.000 - 0.394 in/min	PLC 0; UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	318 - 324 °C	604 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	329 - 343 °C	624 - 649 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Lubricant
	Mold Release
Appearance	Black
	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fast Molding Cycle
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Stiffness
	High Flow
	High Stiffness
	High Strength
	Hot Water Moldability
	Low Moisture Absorption
	Lubricated
Forms	Pellets
Generic	PPA
Processing Method	Water-Heated Mold Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	Bobbins
	Camera Applications
	Cell Phones
	Connectors
	Electrical/Electronic Applications
	General Purpose
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement