Nilit FRIANYL B63 KV30 Nylon 6 for injection molding, 30% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 KV30 Nylon 6 for injection molding, 30% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 14 % | 14 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| 4.00 J/cm² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | |
| 0.500 J/cm² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PE-40MC/000 High Density Polyethylene (HDPE) (discontinued **)
- Solvay Specialty Polymers Algoflon® 25CAR+5CER PTFE; Petroleum Coke and Ceramic Filled (discontinued **)
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH
- Dow Corning XIAMETER® PMCPPMX-0245 Cyclopentasiloxane
- Clariant Renol PURSP0002 Polyurethane Elastomer, Ether Based
- Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536
- Caplinq LINQSTAT™ VCF-40009.5S/2
- Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
- Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy
Copyright © lookpolymers.com All Rights Reserved