Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam AFR682A1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % @Temperature 23.0 °C |
0.600 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 |
| Hardness, H358/30 | 133 MPa | 19300 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U |
| 27.0 kJ/m² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 34 @Load 1.00 kg |
34 @Load 2.20 lb |
CS-17; E2P Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 235 °C | 455 °F | B/120; ISO 306 |
| 235 °C | 455 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
|
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 24.0 kV/mm @Thickness 3.20 mm |
610 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0104 @Frequency 50.0 - 60.0 Hz |
0.0104 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0122 @Frequency 1.00e+6 Hz |
0.0122 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 285 °C | 518 - 545 °F | |
| Melt Temperature | 270 - 285 °C | 518 - 545 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Plaskolite Optix® PL-200 Acrylic Resin (discontinued **)
- Momentive Performance Materials RTV6424 White Adhesive Sealant, Non-Corrosive Paste
- Techmer ES Electrablend® PA6/6 CF20 L BK 20% Carbon Filled
- SABIC Innovative Plastics LNP LUBRICOMP RFP48SXS PA 66 (Europe-Africa-Middle East)
- Borealis BL1481 High Density Polyethylene
- Unitika elitel UE3400 Polyester, Flake
- Hexcel® Redux® 319L High Performance Modified Epoxy Film Adhesive (0.036 psf)
- 3M Scotchcal™ 1000-56 Graphic Film
- Solvay RHODASURF® AAE-10 Surfactant
Copyright © lookpolymers.com All Rights Reserved