Lanxess DurethanÂ® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CoPA, injection molding grade, 30% glass fibers, elastomer-modified, higher impact and notched impact strength and also higher energy absorption under biaxial impact load than BKV 130, conditioning may be unnecessary in single cases, good heat-ageing resistance

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/inÂ³	ISO 1183
Water Absorption	6.0 %	6.0 %	Test Sim. to ISO 62
Moisture Absorption at Equilibrium	1.8 %	1.8 %	23Â°C/50% R.H.; Test Sim. to ISO 62

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.0 MPa	11600 psi	Conditioned; ISO 527-1/-2
	130 MPa	18900 psi	ISO 527-1/-2
Elongation at Break	3.5 %	3.5 %	ISO 527-1/-2
	8.0 %	8.0 %	Conditioned; ISO 527-1/-2
Tensile Modulus	4.40 GPa	638 ksi	Conditioned; ISO 527-1/-2
	8.10 GPa	1170 ksi	ISO 527-1/-2
Charpy Impact Unnotched	9.00 J/cmÂ² @Temperature 23.0 Â°C	42.8 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
	9.50 J/cmÂ² @Temperature -30.0 Â°C	45.2 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	9.50 J/cmÂ² @Temperature -30.0 Â°C	45.2 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eU
	10.0 J/cmÂ² @Temperature 23.0 Â°C	47.6 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eU
Charpy Impact, Notched	2.00 J/cmÂ² @Temperature -30.0 Â°C	9.52 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	2.00 J/cmÂ² @Temperature -30.0 Â°C	9.52 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eA
	2.50 J/cmÂ² @Temperature 23.0 Â°C	11.9 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
	4.50 J/cmÂ² @Temperature 23.0 Â°C	21.4 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eA
Impact	1303	1303	Puncture maximum force (N); ISO 6603-2
	939 @Temperature -30.0 Â°C	939 @Temperature -22.0 Â°F	Puncture maximum force (N); ISO 6603-2
Puncture Energy	7.00 J	5.16 ft-lb	ISO 6603-2
	4.00 J @Temperature -30.0 Â°C	2.95 ft-lb @Temperature -22.0 Â°F	ISO 6603-2
	4.00 J @Temperature -30.0 Â°C	2.95 ft-lb @Temperature -22.0 Â°F	Conditioned; ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 Âµm/m-Â°C	11.1 Âµin/in-Â°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	130 Âµm/m-Â°C	72.2 Âµin/in-Â°F	ISO 11359-1/-2
Melting Point	213 Â°C	415 Â°F	10Â°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	200 Â°C	392 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	190 Â°C	374 Â°F	ISO 75-1/-2
Vicat Softening Point	200 Â°C	392 Â°F	50Â°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	450 V	450 V	IEC 60112

Descriptive Properties	Value	Comments
Features	Heat stabilized or stable to heat
	High impact or high impact modified
Form	Pellets
ISO Shortname	ISO 1874-PA 6/66-HI, MHR, -080, GF30
Processing	Injection molding
Region	Asia Pacific
	Europe
	Near East/Africa
	North America
	South and Central America