SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4830 could be positioned for body panels, safety equipment, housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 266 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 265 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 | |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 | |
| 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 110 % | 110 % | 50 mm/min; ISO 527 |
| 120 % | 120 % | 5 mm/min; ISO 527 | |
| 140 % | 140 % | Type I, 50 mm/min; ASTM D638 | |
| 150 % | 150 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 |
| 4.1 % | 4.1 % | 5 mm/min; ISO 527 | |
| 4.2 % | 4.2 % | 50 mm/min; ISO 527 | |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.40 GPa | 493 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | 2 mm/min; ISO 178 |
| 3.10 GPa | 450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| 1.20 J/cm @Temperature -30.0 °C |
2.25 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 1.50 J/cm @Temperature 0.000 °C |
2.81 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 15.0 kJ/m² @Temperature 0.000 °C |
7.14 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 70.0 J @Temperature 23.0 °C |
51.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 70.0 J @Temperature -20.0 °C |
51.6 ft-lb @Temperature -4.00 °F |
ASTM D3763 | |
| Impact Test | 110 J | 81.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 133 °C | 271 °F | Rate B/50; ASTM D1525 |
| 133 °C | 271 °F | Rate B/50; ISO 306 | |
| 135 °C | 275 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-216-P Powdered Metal
- SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC
- Lubriplate GR-132 Portable Tool Grease Specialty Lubricant and Grease
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.125" thick)
- Westlake LF1021 Butene Linear Low Density Polyethylene
- Zeon Chemicals Zealloy® 1422 Modifier for Thermoplastics
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- Denka VINYKON W4800 PVC, W grade for equipment cords, for heat resistance
- DuPont Performance Polymers Neoprene W-M1 Polychloroprene Rubber
- Advanced Elastomer Systems Santoprene® 283-40 Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved