M Cubed Technologies HSC-702 Aluminum-toughened Reaction Bonded Silicon Carbide

Category	Ceramic , Carbide , Ceramic Matrix Composite
Manufacturer	M Cubed Technologies, Inc
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	M Cubed Technologies HSC-702 Aluminum-toughened Reaction Bonded Silicon Carbide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High fracture tougness reaction bonded SiC. Used in applications that require both high wear and high impact resistance. Bullnoses, fan liners, hydrocyclone liners, etc.Information provided by M Cubed Technologies, Inc.

Physical Properties	Metric	English	Comments
Density	3.02 g/cc	0.109 lb/in³	ASTM C135

Mechanical Properties	Metric	English	Comments
Knoop Microhardness	1000 @Load 2.00 kg	1000 @Load 4.41 lb	kg/mm2; ASTM C1326
Modulus of Elasticity	330 GPa	47900 ksi	ASTM E494
Flexural Strength	260 MPa	37700 psi	ASTM C1161
Poissons Ratio	0.19	0.19	ASTM E494
Fracture Toughness	5.50 MPa-m½	5.01 ksi-in½	ASTM C1421
Shear Modulus	139 GPa	20200 ksi	Calculated

Thermal Properties	Metric	English	Comments
CTE, linear	4.40 µm/m-°C @Temperature 25.0 - 100 °C	2.44 µin/in-°F @Temperature 77.0 - 212 °F	ASTM E831
Thermal Conductivity	200 W/m-K	1390 BTU-in/hr-ft²-°F	ASTM E1461

Descriptive Properties	Value	Comments
Matrix	Al-Si
Particle Reinforcement	SiC
Vol. % Reinforcement	70