SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D 792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 0.750 - 2.30 mm |
0.0080 - 0.011 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.010 - 0.014 cm/cm @Thickness 2.30 - 4.60 mm |
0.010 - 0.014 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.013 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 9.3 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.3 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 26 % | 26 % | Type I, 50 mm/min; ASTM D 638 |
| 30 % | 30 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.15 GPa | 312 ksi | 5 mm/min; ASTM D 638 |
| 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| 2.02 GPa | 293 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.58 J/cm @Temperature -30.0 °C |
2.96 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 5.22 J/cm @Temperature 23.0 °C |
9.78 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 145 °C | 293 °F | Rate B/50; ISO 306 |
| 148 °C | 298 °F | Rate B/50; ASTM D 1525 | |
| 150 °C | 302 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 by SABIC-IP | |
| Oxygen Index | 30 % | 30 % | LOI; ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D 257 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 | |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | pass | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Solvay ABEX® EP 120/K Surfactant
- Chase Plastics CP Pryme® N300L (COND, 50% RH) Nylon 6 (Utility Grade), Internally Lubricant
- Epoxy Technology EPO-TEK® OG159-2 UV Cure Optical Epoxy
- Eurostar Staramide BG6U PA6, 30% Glass Fiber Filled, UV Stabilized, Injection Molded
- CMW® ELKONITE® 1060 Silver Tungsten Carbide Contact Material
- ArcelorMittal HSLA 550 High strength low alloy steel for cold forming, Hot Rolled
- Aremco Ceramabond™ 835 High Temperature Ceramic Adhesive/Paste, Zirconia Filled
- Nye Lubricants UniFlor 8917 (UF) Synthetic Oil
- BP Amoco Accpro® 9433 Enhanced Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved