Polymer Property : Linear Mold Shrinkage, Transverse = 0.012 in/in Product List

Physical Properties

Tips: 30 items are displayed at most.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific)
LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Europe-Africa-Middle East)
LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm
<br>@Time 86400 sec
 0.012 - 0.014 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66
LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm
<br>@Time 86400 sec
 0.012 - 0.014 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific)
LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm
<br>@Time 86400 sec
 0.012 - 0.014 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA
LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized.
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 357 PBT
PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 357 PBT+PC
PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 365 PC+PET
Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"".
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Europe-Africa-Middle East)
Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66
LNP* STAT-KON* REL42 is a compound based on Nylon 66 resin containing 20% PTFE, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6
LNP* THERMOCOMP* PH0460A is a compound based on Nylon 6. Added feature of this material is: High Specific Gravity.
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm
<br>@Time 86400 sec
 0.012 - 0.014 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66
LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66
LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific)
LNP* Thermocomp* RF00AH is a compound based on Nylon 66 resin containing Glass Fiber.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF00AS PA 66
LNP THERMOCOMP* RF00AS is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
<br>@Time 86400 sec
 0.012 - 0.015 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA
LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flam..
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
<br>@Time 86400 sec
 0.012 - 0.015 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA
LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flam..
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA
LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing 40% Glass Fiber. Added feature of this grade is: Healthcare.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP Thermocomp WC006 Polyester, TP
LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Valox® 365 PET
Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031".This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.012 - 0.016 cm/cm
<br>@Thickness 2.30 - 4.60 mm
 0.012 - 0.016 in/in
<br>@Thickness 0.0906 - 0.181 in
 SABIC Method
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific)
Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66
LNP THERMOCOMP* RF002 is a compound based on Nylon 66 resin containing 10% Glass Fiber.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66
LNP THERMOCOMP* RF002 is a compound based on Nylon 66 resin containing 10% Glass Fiber.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66 (Asia Pacific)
LNP* THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA (Asia Pacific)
LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing Glass Fiber.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT
LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP
LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP (Asia Pacific)
LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific)
LNP* Thermocomp* PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Linear Mold Shrinkage, Transverse 0.012 cm/cm
<br>@Time 86400 sec
 0.012 in/in
<br>@Time 24.0 hour
 ISO 294
SABIC Innovative Plastics LNP STAT-KON MFD02 PP (Asia Pacific)
LNP* Stat-kon* MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.