SABIC Innovative Plastics Xenoy® CL402U PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® CL402U PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XENOY CL402U has been specially developed for extrusion blowmoulding applications, where higher melt strength is desired. XENOY CL402U is a high impact material combined with good UV resistance performance. This grade is a CL402 with improved UV-performance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | on tensile bar; SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 7.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 85.0 MPa | 12300 psi | ISO 2039-1 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 39.0 kJ/m² @Temperature -40.0 °C |
18.6 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A |
| 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 47.0 kJ/m² @Temperature -20.0 °C |
22.4 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 53.0 kJ/m² @Temperature 23.0 °C |
25.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C | |
| Taber Abrasion, mg/1000 Cycles | 40 @Load 1.00 kg |
40 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C @Temperature 23.0 - 80.0 °C |
58.3 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature 23.0 - 80.0 °C |
58.3 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ISO 306 |
| 125 °C | 257 °F | Rate B/120; ISO 306 | |
| 155 °C | 311 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 18.0 kV/mm @Thickness 1.60 mm |
457 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ 9570-9 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Lexan® HPS1S PC
- NOVA Chemicals Sclair® 35BP HDPE Extrusion Resin, 2.2% Carbon Black Filled (discontinued **)
- Grupo Repol Dinalon® B1S25 B30 PA6 30% Glass Beads
- A. Schulman POLYAXIS® PD8020 Polypropylene
- A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene
- Hexcel® HexWeb® CR-PAA™ 5/32-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb
- CMW® ELKONITE® 30W3 Infiltrated Copper Tungsten contact material ASTM B702, Class E, infiltrated, RWMA Class 12
- 3M FP080 Clear Polypropylene Label Products
- ArcelorMittal HSLA 340 High strength low alloy steel for cold forming, Cold Rolled
Copyright © lookpolymers.com All Rights Reserved