SABIC Innovative Plastics Xenoy® 6370 PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 6370 PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Water Absorption | 0.090 % @Time 86400 sec |
0.090 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 0.750 - 2.30 mm |
0.0030 - 0.0040 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.0040 - 0.0050 cm/cm @Thickness 2.30 - 4.60 mm |
0.0040 - 0.0050 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm @Thickness 0.750 - 2.30 mm |
0.0040 - 0.0070 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.0070 - 0.0090 cm/cm @Thickness 2.30 - 4.60 mm |
0.0070 - 0.0090 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Melt Flow | 24 g/10 min @Load 5.00 kg, Temperature 250 °C |
24 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
12 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 19 g/10 min @Load 5.00 kg, Temperature 265 °C |
19 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 91.0 MPa | 13200 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D638 |
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 105 % | 105 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 9.75 GPa | 1410 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 154 MPa | 22300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.37 GPa | 779 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.75 GPa | 1120 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| 1.12 J/cm @Temperature -30.0 °C |
2.10 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature 60.0 - 138 °C |
11.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 6.40 mm |
300 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ISO 306 |
| 150 °C | 302 °F | Rate B/120; ISO 306 | |
| 153 °C | 307 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.80e+15 ohm-cm | 4.80e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
ASTM D150 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in air; ASTM D149 |
| 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
ASTM D150 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.7cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- Lanxess Durethan® A 30 H2.0 901510 Nylon 66
- LyondellBasell PNB Propylene glycol normal butyl ether
- Samsung Cheil Industries Starex® SV-0157 ABS, Unreinforced Extrusion Grade
- Teknor Apex Flexalloy® 9100-65 Polyvinyl Chloride Elastomer
- Dow DOWLEX™ IP-50 High Density Polyethylene
- Ashley Polymers Ashlene® 527-25G Nylon 66, 25% Glass Reinforced
- Total Lacqrene® 6631 Impact Polystyrene (discontinued **)
- Arlon R37503G015 0.015" (0.381 mm) Cured Fluorosilicone Rubber
- Lushan M-12A Adhesive Resin for Multi-layer Oxygen Barrier Pipe
Copyright © lookpolymers.com All Rights Reserved