DuPont Performance Polymers Zytel® FG408L NC010 Nylon 66 (Unverified Data**)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer	DuPont Performance Polymers
Trade Name	Zytel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Zytel® FG408L NC010 Nylon 66 (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Unreinforced Toughened Polyamide 66 with Developed for Food Contact Applications Zytel FG408L NC010 is a general purpose lubricated impact modified polyamide 66 resin with superior toughness for injection molding applications. It has been developed forInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³
	1.09 g/cc	0.0394 lb/in³	DAM; ISO 1183
Water Absorption	7.0 % @Thickness 2.00 mm	7.0 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.20 % @Thickness 2.00 mm	2.20 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Test	150 cm³/g	150 cm³/g	DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow	0.015 cm/cm	0.015 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	DAM; ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	43.0 MPa	6240 psi	50%RH; ISO 527-1/-2
	61.0 MPa	8850 psi	DAM; ISO 527-1/-2
Elongation at Break	35 %	35 %	DAM; Nominal; ISO 527-1/-2
	>= 50 %	>= 50 %	50%RH; Nominal; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	DAM; ISO 527-1/-2
	6.0 %	6.0 %	DAM; ISO 527-3
	26 %	26 %	50%RH; ISO 527-1/-2
Tensile Modulus	1.10 GPa	160 ksi	50%RH; ISO 527-1/-2
	2.20 GPa	319 ksi	DAM; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	DAM; ISO 179/1eU
	NB	NB	50%RH; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DAM; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	1.50 J/cm²	7.14 ft-lb/in²	DAM; ISO 179/1eA
	2.50 J/cm²	11.9 ft-lb/in²	50%RH; ISO 179/1eA
	0.800 J/cm² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	1.50 J/cm² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour	950 MPa @Time 3600 sec	138000 psi @Time 1.00 hour	50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours	840 MPa @Time 3.60e+6 sec	122000 psi @Time 1000 hour	50%RH; ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	132 µm/m-°C	73.3 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	132 µm/m-°C	73.3 µin/in-°F	DAM; ISO 11359-1/-2
Specific Heat Capacity	2.60 J/g-°C	0.621 BTU/lb-°F
Thermal Conductivity	0.160 W/m-K	1.11 BTU-in/hr-ft²-°F	of melt
Melting Point	263 °C	505 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	155 °C	311 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	66.0 °C	151 °F	DAM; ISO 75-1/-2
Vicat Softening Point	210 °C	410 °F	DAM; 50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	DAM; IEC 60695-11-10
Oxygen Index	19 %	19 %	DAM; ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	50%RH; IEC 60093
	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	DAM; IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	50%RH; IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	3.2 @Frequency 100 Hz	3.2 @Frequency 100 Hz	DAM; IEC 60250
	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	7.0 @Frequency 100 Hz	7.0 @Frequency 100 Hz	50%RH; IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	DAM; IEC 60243-1
Dissipation Factor	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	DAM; IEC 60250
	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	0.050 @Frequency 1.00e+6 Hz	0.050 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	0.15 @Frequency 100 Hz	0.15 @Frequency 100 Hz	50%RH; IEC 60250
Comparative Tracking Index	600 V	600 V	DAM; IEC 60112

Descriptive Properties	Value	Comments
Additives	Release agent
Delivery Form	Pellets
Part Marking Code	>PA66-I<	ISO 11469
Processing	Injection Moulding
	Profile Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66-I