SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D792
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Filler Content 10 %
10 %
ASTM D229
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.27 %
0.27 %
ISO 62
Viscosity 90000 cP
90000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0060 - 0.010 cm/cm
0.0060 - 0.010 in/in
on Tensile Bar; SABIC Method
Linear Mold Shrinkage, Transverse 0.0070 - 0.012 cm/cm
0.0070 - 0.012 in/in
on Tensile Bar; SABIC Method
Melt Flow 110 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 110 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 17 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
55 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 55 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
90 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 90 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 87.0 MPa
12600 psi
Type I, 5 mm/min; ASTM D638
90.0 MPa
13100 psi
5 mm/min; ISO 527
Tensile Strength, Yield 87.0 MPa
12600 psi
Type I, 5 mm/min; ASTM D638
90.0 MPa
13100 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 3.0 %
3.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 5.30 GPa
769 ksi
5 mm/min; ASTM D638
5.40 GPa
783 ksi
1 mm/min; ISO 527
Flexural Strength 125 MPa
18100 psi
1.3 mm/min, 50 mm span; ASTM D790
135 MPa
19600 psi
2 mm/min; ISO 178
Flexural Yield Strength 125 MPa
18100 psi
1.3 mm/min, 50 mm span; ASTM D790
140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Modulus 4.00 GPa
580 ksi
1.3 mm/min, 50 mm span; ASTM D790
4.50 GPa
653 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
0.500 J/cm

@Temperature 0.000 °C
 0.937 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.500 J/cm

@Temperature -30.0 °C
 0.937 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 4.00 J/cm
7.49 ft-lb/in
ASTM D4812
3.15 J/cm

@Temperature -30.0 °C
 5.90 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature 0.000 °C
 2.38 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.30 J/cm²
15.7 ft-lb/in²
ISO 179/2C
2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.80 J/cm²

@Temperature -30.0 °C
 13.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²
2.86 ft-lb/in²
ISO 179/2C
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Taber Abrasion, mg/1000 Cycles 45
45
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 41.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
45.5 µm/m-°C

@Temperature 23.0 - 150 °C
 25.3 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
50.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 27.8 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 72.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
160 µm/m-°C

@Temperature 23.0 - 80.0 °C
 88.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
176 µm/m-°C

@Temperature 23.0 - 150 °C
 97.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
215 °C
419 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
215 °C

@Thickness 3.20 mm
 419 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
190 °C
374 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
190 °C

@Thickness 3.20 mm
 374 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 202 °C
396 °F
Rate B/120; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A