Aclo Accutech Polypropylene Copolymer CP0436T10L Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436T10L Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 62 | 62 | ASTM D785 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.300 GPa | 188.5 ksi | ASTM D638 |
| Flexural Strength | 27.0 MPa | 3920 psi | ASTM D790 |
| Flexural Modulus | 1.150 GPa | 166.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 1-D Heavy Oil Plasticizer
- LG Chemical Lupox® SG3250A PBT+PET+MF25%
- Kolon KOPA® KN178MT40 M/F Reinforced Nylon 6
- Struktol V-SSE Processing Additive
- Addiplast Addinyl B2 V50 Nylon 6, 50% Glass Filled
- Arkema Group Orgalloy® LT 4060ISH Flexible Nylon Alloy (Conditioned)
- Bostik 2105 Low viscosity, short open time EVA Glue Stick
- Techmer ES HiFill FR® PA6/6 FR HS
Copyright © lookpolymers.com All Rights Reserved