SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Filler Content | 6.0 % | 6.0 % | ASTM D229 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Viscosity | 110000 cP | 110000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| 0.0060 - 0.016 cm/cm <br>@Thickness 3.20 mm |
0.0060 - 0.016 in/in <br>@Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 13 g/10 min <br>@Load 1.20 kg,<br> Temperature 250 °C |
13 g/10 min <br>@Load 2.65 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min <br>@Load 1.20 kg,<br> Temperature 250 °C |
11 g/10 min <br>@Load 2.65 lb,<br> Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 18 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C |
18 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 46 g/10 min <br>@Load 5.00 kg,<br> Temperature 250 °C |
46 g/10 min <br>@Load 11.0 lb,<br> Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 117 MPa | 17000 psi | ISO 2039-1 |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.5 % | 3.5 % | 5 mm/min; ISO 527 | |
| 6.0 % | 6.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
| 4.70 GPa | 682 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 115 MPa | 16700 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| 4.10 GPa | 595 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| 0.690 J/cm <br>@Temperature -30.0 °C |
1.29 ft-lb/in <br>@Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² <br>@Temperature -30.0 °C |
2.38 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 28.0 kJ/m² <br>@Temperature -30.0 °C |
13.3 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/2C |
| 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 3.50 J/cm² <br>@Temperature -30.0 °C |
16.7 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 179/2C | |
| 4.00 J/cm² <br>@Temperature -30.0 °C |
19.0 ft-lb/in² <br>@Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/2C | |
| 0.400 J/cm² <br>@Temperature -30.0 °C |
1.90 ft-lb/in² <br>@Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.500 J/cm² <br>@Temperature -30.0 °C |
2.38 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 3.00 J <br>@Temperature 23.0 °C |
2.21 ft-lb <br>@Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.0 µm/m-°C <br>@Temperature 23.0 - 80.0 °C |
33.3 µin/in-°F <br>@Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C <br>@Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F <br>@Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| 85.0 µm/m-°C <br>@Temperature 23.0 - 150 °C |
47.2 µin/in-°F <br>@Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 215 °C | 419 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 170 °C | 338 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 150 °C <br>@Thickness 3.20 mm |
302 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 204 °C | 399 °F | Rate B/120; ISO 306 |
| 206 °C | 403 °F | Rate B/50; ISO 306 | |
| 206 °C | 403 °F | Rate B/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0 <br>@Frequency 1.00e+6 Hz |
3.0 <br>@Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 <br>@Frequency 50.0 - 60.0 Hz |
3.1 <br>@Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm <br>@Thickness 3.20 mm |
432 kV/in <br>@Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.0 kV/mm <br>@Thickness 1.60 mm |
635 kV/in <br>@Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 30.0 kV/mm <br>@Thickness 0.800 mm |
762 kV/in <br>@Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 <br>@Frequency 50.0 - 60.0 Hz |
0.0010 <br>@Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.014 <br>@Frequency 1.00e+6 Hz |
0.014 <br>@Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 150 V | >= 150 V | IEC 60112 |
| 250 V | 250 V | IEC 60112 |
Users viewing this material also viewed the following:
- Nye Lubricants 181UV (SO) Synthetic Oil
- SABIC Innovative Plastics Lexan® OQ4320R PC
- Polimeri Europa Extir® CM Giotto 5 Expandable Polystyrene - Continuous Mass
- Chevron Phillips EB6025 HIPS - High Impact Polystyrene (discontinued **)
- Hong Kun Group 2,4,6-Trichloropyrimidine Pharmaceutical Intermediate
- Schott N-LASF45 Glass
- A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene
- ExxonMobil 630 Mobil SHC 600 Series
- Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM
Copyright © lookpolymers.com All Rights Reserved