SABIC Innovative Plastics NORYL SE100 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL SE100 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL® SE100 is an unfilled, flame retardant material with a Vicat B/120 of 120°C. It has a UL-94 flammability rating V1 @ 1.47 mm, and is halogen free according to VDE/DIN 472 part 815.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 15 g/10 min @Load 3.80 kg, Temperature 280 °C |
15 g/10 min @Load 8.38 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 87.0 MPa | 12600 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 65 | 65 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 105 °C | <= 221 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 110 °C | 230 °F | Rate B/50; ISO 306 |
| 115 °C | 239 °F | Rate B/120; ISO 306 | |
| 120 °C | 248 °F | Rate A/50; ISO 306 | |
| UL RTI, Electrical | 95.0 °C | 203 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 31 % | 31 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.6 @Frequency 50.0 - 60.0 Hz |
2.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 26.0 kV/mm @Thickness 1.60 mm |
660 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm |
838 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0080 @Frequency 50.0 - 60.0 Hz |
0.0080 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Niche Polymer PA6GF43N Nylon 6, 43% Glass Fiber Filled
- PTS PCA-2201NH Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy
- Techmer ES HiFill® HDPE LGF50 12 mm 50% Glass Filled
- Styron SE PB-5800 Schkopau Low-cis Polybutadiene Rubber (PBR)
- Solvay SOPROPHOR® 796/85 Surfactant
- Unitika A3130 PA6, 35% Mineral Reinforced, Dry
- A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer
- DuPont Performance Polymers Zytel® 70G35NOX BK309 Nylon 66
- Dymax 956 Potting and Encapsulation Adhesive
- Arlon HS930-10R##-P4 0.030" (0.762 mm) Self-Fusing Silicone Tape (Rectangular, Unsupported)
Copyright © lookpolymers.com All Rights Reserved