Material Notes:

Noryl* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Density	1.14 g/cc	0.0412 lb/inÂ³	ISO 1183
Moisture Absorption	0.0500 %	0.0500 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.25 %	0.25 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	22 g/10 min @Load 5.00 kg, Temperature 250 Â°C	22 g/10 min @Load 11.0 lb, Temperature 482 Â°F	ASTM D1238
Melt Index of Compound	22 g/10 min @Load 5.00 kg, Temperature 250 Â°C	22 g/10 min @Load 11.0 lb, Temperature 482 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	39.0 MPa	5660 psi	Type I, 50 mm/min; ASTM D638
	40.0 MPa	5800 psi	50 mm/min; ISO 527
Tensile Strength, Yield	51.0 MPa	7400 psi	50 mm/min; ISO 527
	54.0 MPa	7830 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	20 %	20 %	Type I, 50 mm/min; ASTM D638
	20 %	20 %	50 mm/min; ISO 527
Elongation at Yield	3.0 %	3.0 %	50 mm/min; ISO 527
	3.5 %	3.5 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.30 GPa	334 ksi	1 mm/min; ISO 527
	2.50 GPa	363 ksi	5 mm/min; ASTM D638
Flexural Yield Strength	73.0 MPa	10600 psi	2 mm/min; ISO 178
	85.0 MPa	12300 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.25 GPa	326 ksi	2 mm/min; ISO 178
	2.60 GPa	377 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.30 J/cm	2.44 ft-lb/in	ASTM D256
	0.750 J/cm @Temperature -30.0 Â°C	1.41 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
	4.00 kJ/mÂ² @Temperature -30.0 Â°C	1.90 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	0.700 J/cmÂ²	3.33 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	19.0 J @Temperature 23.0 Â°C	14.0 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	70.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	70.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	70.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	85.0 Â°C @Thickness 3.20 mm	185 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	72.0 Â°C	162 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	72.0 Â°C @Thickness 3.20 mm	162 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	93.0 Â°C	199 Â°F	Rate B/50; ASTM D1525
	93.0 Â°C	199 Â°F	Rate B/50; ISO 306
	96.0 Â°C	205 Â°F	Rate B/120; ISO 306
UL RTI, Electrical	95.0 Â°C	203 Â°F	UL 746B
UL RTI, Mechanical with Impact	80.0 Â°C	176 Â°F	UL 746B
UL RTI, Mechanical without Impact	95.0 Â°C	203 Â°F	UL 746B
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94 by SABIC-IP
	5VB @Thickness 2.50 mm	5VB @Thickness 0.0984 in	UL 94 by SABIC-IP