Samsung Cheil Industries Starex® SD-0150UF ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SD-0150UF ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 220 °C |
11 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 31.4 MPa | 4550 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 16 % | 16 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 58.8 MPa | 8530 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.84 J/cm @Thickness 6.35 mm |
5.33 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 3.53 J/cm @Thickness 3.17 mm |
6.61 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | B/50; ISO R306 |
| 99.0 °C | 210 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® S701S ABS (Europe-Africa-Middle East)
- Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant
- Magyar Aluminum ALOLT 730 Aluminum Hydroxide
- Freudenberg Simrit N475 Nitrile Elastomer (NBR)
- A. Schulman POLYTROPE™ TPP 503 Injection Molding Grade Olefinic Thermoplastic Elastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N650 Filler
- ExxonMobil LD 144.50 Packaging Film Resin
- AKG Polymers Vision PP PPC TC3005 Polypropylene Copolymer Compound
- Asahi Kasei Xyron® G703V Modified Polyphenylene Ether
- Borealis LE6025 Polyethylene Modified Jacketing Compound
Copyright © lookpolymers.com All Rights Reserved