Victrex® PEEK -HT™ 22GL30 Polyetherketone, 30% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyketone
Manufacturer	Victrex
Trade Name	PEEK
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® PEEK -HT™ 22GL30 Polyetherketone, 30% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description:High performance thermoplastic material, 30% glass fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Higher temperature applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®

Physical Properties	Metric	English	Comments
Density	1.53 g/cc	0.0553 lb/in³	Crystalline; ISO 1183
Water Absorption at Saturation	0.50 % @Temperature 23.0 °C	0.50 % @Temperature 73.4 °F	Equilibrium; by immersion; ISO 62-1
	0.60 % @Temperature 100 °C	0.60 % @Temperature 212 °F	ISO 62-1
Viscosity	450000 cP @Temperature 400 °C	450000 cP @Temperature 752 °F	melt; ISO 11443
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	395°C nozzle, 200°C tool; ISO 294-4
Spiral Flow	10.5 cm @Thickness 1.00 mm	4.13 in @Thickness 0.0394 in	395°C nozzle, 200°C tool

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	88 @Temperature 23.0 °C	88 @Temperature 73.4 °F	ISO 868
Tensile Strength at Break	55.0 MPa @Temperature 275 °C	7980 psi @Temperature 527 °F	ISO 527
	65.0 MPa @Temperature 225 °C	9430 psi @Temperature 437 °F	ISO 527
	75.0 MPa @Temperature 175 °C	10900 psi @Temperature 347 °F	ISO 527
	125 MPa @Temperature 125 °C	18100 psi @Temperature 257 °F	ISO 527
	200 MPa @Temperature 23.0 °C	29000 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.9 % @Temperature 23.0 °C	2.9 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	12.0 GPa @Temperature 23.0 °C	1740 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	85.0 MPa @Temperature 275 °C	12300 psi @Temperature 527 °F	ISO 178
	120 MPa @Temperature 175 °C	17400 psi @Temperature 347 °F	ISO 178
	210 MPa @Temperature 123 °C	30500 psi @Temperature 253 °F	ISO 178
	290 MPa @Temperature 23.0 °C	42100 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	11.0 GPa @Temperature 23.0 °C	1600 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	50.0 MPa @Temperature 250 °C	7250 psi @Temperature 482 °F	ISO 604
	75.0 MPa @Temperature 200 °C	10900 psi @Temperature 392 °F	ISO 604
	180 MPa @Temperature 120 °C	26100 psi @Temperature 248 °F	ISO 604
	290 MPa @Temperature 23.0 °C	42100 psi @Temperature 73.4 °F	ISO 604
Izod Impact, Notched (ISO)	11.0 kJ/m² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Izod Impact, Unnotched (ISO)	70.0 kJ/m² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	ISO 180/U
Charpy Impact Unnotched	7.00 J/cm² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	SO 179/1U
Charpy Impact, Notched	0.900 J/cm² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	45.0 µm/m-°C @Temperature <=152 °C	25.0 µin/in-°F @Temperature <=306 °F	Average below Tg; ISO 11359
	110 µm/m-°C @Temperature >=152 °C	61.1 µin/in-°F @Temperature >=306 °F	Average above Tg; ISO 11359
CTE, linear, Parallel to Flow	20.0 µm/m-°C @Temperature <=152 °C	11.1 µin/in-°F @Temperature <=306 °F	Below Tg; ISO 11359
	25.0 µm/m-°C @Temperature >=152 °C	13.9 µin/in-°F @Temperature >=306 °F	Above Tg; ISO 11359
Thermal Conductivity	0.300 W/m-K @Temperature 23.0 °C	2.08 BTU-in/hr-ft²-°F @Temperature 73.4 °F	Average; ISO/CD 22007-4
	0.350 W/m-K @Temperature 23.0 °C	2.43 BTU-in/hr-ft²-°F @Temperature 73.4 °F	Along flow; ISO 22007-4
Melting Point	373 °C	703 °F	ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)	360 °C	680 °F	ISO 75-f
Glass Transition Temp, Tg	152 °C	306 °F	Onset; ISO 11357
	160 °C	320 °F	Midpoint; ISO 11357
Glow Wire Test	960 °C @Thickness 2.00 mm	1760 °F @Thickness 0.0787 in	IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	IEC 60093
Dielectric Constant	3.2 @Frequency 1000 Hz, Temperature 23.0 °C	3.2 @Frequency 1000 Hz, Temperature 73.4 °F	IEC 60250
Dielectric Strength	23.0 kV/mm @Thickness 2.00 mm	584 kV/in @Thickness 0.0787 in	IEC 60243-1
Dissipation Factor	0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	IEC 60250
Comparative Tracking Index	150 V	150 V	IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	<= 100 °C	<= 212 °F	Hopper Temperature
Nozzle Temperature	395 °C	743 °F
Mold Temperature	190 - 215 °C	374 - 419 °F
Drying Temperature	120 °C @Time 18000 sec	248 °F @Time 5.00 hour
	150 °C @Time 10800 sec	302 °F @Time 3.00 hour