- SABIC Innovative Plastics NORYL NH7111E PPE+HIPS
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH7111E PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR additives to achieve a V1 UL94 rating at 1.6 mm and V0 UL94 at 3.00mm with a CTI value of 400 V. Noryl EXNL0280 may be an excellent material candidate for application requiring electrically insulating properties, low moisture absorption, low warpage and thin wall flame resistance. Available in limited light grey colors
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.23 % | 0.23 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 300 °C |
18 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 280 °C |
15 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
| 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.60 GPa | 522 ksi | 5 mm/min; ASTM D638 |
| 3.79 GPa | 550 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 127 MPa | 18400 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.57 GPa | 518 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.62 GPa | 525 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 43.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 149 °C | 300 °F | Rate B/50; ASTM D1525 |
| 155 °C | 311 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.00 mm |
V-1 @Thickness 0.0394 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 775 °C | 1430 °F | IEC 60695-2-13 | |
| 775 °C | 1430 °F | IEC 60695-2-13 | |
| 775 °C | 1430 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0e+14 - 1.0e+16 ohm-cm | 1.0e+14 - 1.0e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 3.00e+13 - 5.00e+13 ohm | 3.00e+13 - 5.00e+13 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 27.3 kV/mm @Thickness 3.20 mm |
693 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD104R PC
- Minelco FordaDol Dolomite
- Silberline Extra Sparkle Silvet® 300-10-E1
- Styrolution Absolac® XT04M ABS
- A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound
- Beijing Evergrow Resources BF-20 Basalt Needle Felt
- BASF Sicopal® Yellow L 1100 Color Additive
- Arkema Group Oroglas® VM Acrylic, Injection Molding Grade (discontinued **)
- SABIC Innovative Plastics NORYL APS130 PPE+PPS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved