SABIC Innovative Plastics NORYL HN731A PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL HN731A PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant (restrictions apply). Combines good hydrolytic stability and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.23 % | 0.23 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.2 g/10 min @Load 5.00 kg, Temperature 280 °C |
9.2 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 28.1 % | 28.1 % | Type I, 50 mm/min; ASTM D638 |
| 30 % | 30 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| 7.2 % | 7.2 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.86 GPa | 415 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| 89.0 MPa | 12900 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| 2.42 GPa | 351 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 2.64 GPa | 383 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.13 J/cm | 3.99 ft-lb/in | ASTM D256 |
| 1.33 J/cm @Temperature -40.0 °C |
2.49 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Gardner Impact | 5.00 J @Temperature -40.0 °C |
3.69 ft-lb @Temperature -40.0 °F |
ASTM D3029 |
| 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
ASTM D3029 | |
| Dart Drop, Total Energy | 48.0 J @Temperature 23.0 °C |
35.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 91.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ISO 306 |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 148 °C | 298 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Oxygen Index | 22 % | 22 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.65 @Frequency 50.0 - 60.0 Hz |
2.65 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 21.6 kV/mm @Thickness 3.20 mm |
549 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.00040 @Frequency 50.0 - 60.0 Hz |
0.00040 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Okulen® 500 PE-HMW, Coloured
- Global MPP-120-C 20% Mica Reinforced Polypropylene
- Multibase Multi-Flex® A 8502 A Black TPE Thermoplastic Elastomer
- Wieland Portagold Casting Alloy
- Dow ASPUN™ 6830A Linear Low-Density Polyethylene (LLDPE)
- Dow Nordel® IP 4640 EPDM Hydrocarbon Rubber
- Elisto THERMOSTAR® MD 130 Pattern material
- Colorite Polymers CS1542OR Wire and Cable Jacket Vinyl Compound
- Arlon R34332X039 0.039" (0.991 mm) Fully Cured/Unsupported
- ChevronTexaco GST® EP ISO 32 Oil
Copyright © lookpolymers.com All Rights Reserved