- Polymer Property : Tensile Strength at Break = 49.0 MPa
Polymer Property : Tensile Strength at Break = 49.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS
Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS (Asia Pacific)
Cycoloy* CX7510 resin is an injection moldable, flame retardant PC/ABS blend, with non-chlorinated & non-brominated flame retardants. Key features of Cycoloy CX7510 resin include high heat, high flo..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Cycoloy® CY6120 PC+ABS (Asia Pacific)
Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
|
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® FXG1414T PC Copolymer
PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Europe-Africa-Middle East)
LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® FXD9810 PC Copolymer (Europe-Africa-Middle East)
Non-chlorinated, non-brominated Flame retardant PC-siloxane copolymer blend. Excellent processability, super high flow, good impact, UL rated V-0. Limited translucent colors.This data was supplied b..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | DIN 53504 |
|
Huntsman IROGRAN® A 85 D 4968 Polyester-Based TPU-Injection Extrusion Grade
High Hydrolysis resistance and good crystallinity. Suggested for extrusion.Information provided by Huntsman
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP DX07404H PC
LNP* LUBRICOMP* DX07404H is a compound based on Polycarbonate containing Proprietary Fillers. Added features of this grade are: Healthcare, Wear Resistant.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific)
LNP* Lubricomp* IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer
LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Asia Pacific)
LNP* Lubricomp* KG002 is a compound based on Acetal Copolymer resin containing Graphite Powder. Added features of this material include: Internally Lubricated.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66
LNP* LUBRICOMP* RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D 638 |
|
SABIC Innovative Plastics LNP Stat-kon DX92440 PC
LNP STAT-KON* DX92440 is a compound based on Polycarbonate resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Xenoy® CL101 PBT+PC (Europe-Africa-Middle East)
Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applica..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC
LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP TF006 PU
LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Asia Pacific)
LNP* Stat-loy* N30009 is a compound based on PC+ABS Blend resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS (Asia Pacific)
LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin containing Anti-Static, Flame Retardant. Added features of this material include: Antistat.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
|
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC
LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP MX92284 PP
LNP* THERMOCOMP* MX92284 is a compound based on Polypropylene resin containing Proprietary Filler(s).
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS
LNP* THERMOCOMP* PCA-F-1001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics LNP Thermocomp WB008 PBT
LNP* Thermocomp* WB008 is a compound based on Thermoplastic Polyester (PBT) containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
|
Supreme Petrochem SC 202EL General Purpose Polystyrene
CharacteristicsHigh strength grade Excellent process ability Reduces processing cycle timeProcessing MoldingApplicationsAudio cassettes housing and covers, CD jewel boxes Medical products like disp..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics NORYL FP6130 PPE+PS (Asia Pacific)
Noryl* FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR a..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
Unitika elitel UE3216 Polyester, Pellet
Low Tg type UE3215UNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adhesives, paints, ink binders, and modi..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
|
Unitika elitel UE3620 Polyester, Pellet
High elongation type UE3215UNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adhesives, paints, ink binders,..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics NORYL FXN119BK PPE+HIPS (Asia Pacific)
Noryl* FXN119BK is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BKBK is available in black only.
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Europe-Africa-Middle East)
Noryl FXN119LG is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119LG is available in mutliple colors.This da..
|
|||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER (Asia Pacific)
Polyester+PC alloy. Diffusion Effect. Color package may affect performance.
|
|||