SABIC Innovative Plastics NORYL FP6130 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FP6130 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm with a specific density of 1.1 g/cm^3. Noryl FP6130 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.13 % | 0.13 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 15 g/10 min @Load 1.20 kg, Temperature 280 °C |
15 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 34 g/10 min @Load 2.16 kg, Temperature 280 °C |
34 g/10 min @Load 4.76 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 7.3 % | 7.3 % | Type I, 50 mm/min; ASTM D638 |
| 8.0 % | 8.0 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.51 GPa | 364 ksi | 1 mm/min; ISO 527 |
| 3.14 GPa | 455 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.42 GPa | 351 ksi | 2 mm/min; ISO 178 |
| 2.77 GPa | 402 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| 0.270 J/cm @Temperature -30.0 °C |
0.506 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 110 °C | 230 °F | Rate B/50; ASTM D1525 |
| 111 °C | 232 °F | Rate B/50; ISO 306 | |
| 114 °C | 237 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| Oxygen Index | 30 % | 30 % | ISO 4589 |
| Glow Wire Test | 725 °C | 1340 °F | IEC 60695-2-13 |
| 725 °C | 1340 °F | IEC 60695-2-13 | |
| 725 °C | 1340 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 - 4.50e+16 ohm-cm | 4.00e+16 - 4.50e+16 ohm-cm | ASTM D257 |
| 4.00e+16 - 4.50e+16 ohm-cm | 4.00e+16 - 4.50e+16 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 - 1.50e+14 ohm | 1.00e+14 - 1.50e+14 ohm | ASTM D257 |
| 1.00e+14 - 1.50e+14 ohm | 1.00e+14 - 1.50e+14 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 28.6 kV/mm @Thickness 1.60 mm |
726 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| 250 V | 250 V | IEC 60112 | |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Instrumented Impact Total Energy, 23°C | naJ | ASTM D3763 |
Users viewing this material also viewed the following:
- Paratherm Corporation Paratherm™ GLT™ Heat Transfer Fluid
- Parker Chomerics THERM-A-GAP™ GEL 30 High Performance Fully Cured Dispensable Gel
- Global PPC-0320 Standard Grade Polypropylene
- Indorama Ventures Mexico Polyclearâ„¢ Preserve 2201 PET Resin
- Gromax BFG45-DN00N1 Nylon 6 46% Glass Filled (Conditioned)
- Solvay ANTAROX® LF 224 Surfactant
- Asahi Kasei Tenac® LT200 Homopolymer Acetal Resin
- ATI Allegheny Ludlum Allcorr® Nickel-Based, Corrosion Resistant Alloy
- Lubrizol Advanced Materials Pearlbond® 539 Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved