Aclo Accutech Polypropylene Copolymer CP0436C30L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436C30L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 62 | 62 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 1.300 GPa | 188.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F |
Users viewing this material also viewed the following:
- RheTech Products G40P100-04UV 40% Glass Fiber Reinforced Polypropylene, UV Stabilized, White
- PolyOne Geon™ 210 Series 218 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- PolyOne Geon™ 120 Series 124A Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Gichem GILAC A50VX35/VO ABS Flame Retardant (discontinued **)
- Karina E 898-08/175-IS-RG Beige PVC Compound
- Haynes Hastelloy® S alloy, weld metal, aged 4000 hours
- Shandong Dongyue Shenzhou New Material Co CHFM 175 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- Sharadaa Ceramics REFCAST LC45 Low Cement Castables
- Styrolution PS 1600 GPPS
- Eurotec® Tecomid® NB40 GB30 NL PA6, 30% glass bead reinforced, natural
Copyright © lookpolymers.com All Rights Reserved