SABIC Innovative Plastics Lexan® FXD9810U PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXD9810U PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate with high flow, excellent processability, good impact and thermal properties, UV stabilized, non-Chlorine and non-Bromine flame retardant, UL rated V-0 and V-1. Available in limited diffusion/translucent colors only.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.26 %

@Temperature 23.0 °C
 0.26 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 29 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 29 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
30 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 30 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Elongation at Break 95 %
95 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
2.20 GPa
319 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.00 J/cm

@Temperature -30.0 °C
 3.75 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
6.80 J/cm

@Temperature 23.0 °C
 12.7 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
63.0 kJ/m²

@Temperature 23.0 °C
 30.0 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 180 kJ/m²

@Temperature -30.0 °C
 85.7 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
181 kJ/m²

@Temperature 23.0 °C
 86.1 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched 13.2 J/cm²

@Temperature -30.0 °C
 62.8 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
13.3 J/cm²

@Temperature 23.0 °C
 63.3 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.80 J/cm²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.20 J/cm²

@Temperature 23.0 °C
 29.5 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 63.0 J

@Temperature 23.0 °C
 46.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 38.3 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 37.8 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 131 °C
268 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
130 °C

@Thickness 3.20 mm
 266 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
118 °C

@Thickness 3.20 mm
 244 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 136 °C
277 °F
Rate B/50; ASTM D 1525
137 °C
279 °F
Rate B/50; ISO 306
138 °C
280 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.20 mm
 V-1

@Thickness 0.0472 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
ASTM D 257
Surface Resistance 1.00e+15 - 1.00e+16 ohm
1.00e+15 - 1.00e+16 ohm
ASTM D 257
Comparative Tracking Index 175 - 250 V
175 - 250 V
PLC code 3; UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
PLC code 3; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2