Inno-Comp INNOPOL® CS 1-3140 40% Talc-Filled Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 1-3140 40% Talc-Filled Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 1-3140 is a 40% talc-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-3140 is recommended especially for producing products, where high stiffness, low shrinkage, long term heat stability and good processability are required.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.22 g/cc

@Temperature 23.0 °C
 0.0441 lb/in³

@Temperature 73.4 °F
 ISO 1183
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 4.00 GPa
580 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 4.10 GPa
595 ksi
2 mm/min; ISO 178
Charpy Impact, Notched 0.150 J/cm²

@Temperature -20.0 °C
 0.714 ft-lb/in²

@Temperature -4.00 °F
 ISO 179/1eA
0.250 J/cm²

@Temperature 23.0 °C
 1.19 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
ISO 75-1,-2
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 FMVSS 302
Descriptive Properties Value Comments
Color Natural