LG Chemical LUCON 6080EX ABS+CF
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON 6080EX ABS+CF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, ABS+CF, Electrostatic Dissipation, Wide Processing RangeApplication: Carrying Cart Pipe Coating, BLU carrying TrayCAS No. 9003-56-9, 9003-54-7 and 7782-42-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 220 °C |
10 g/10 min @Load 4.76 lb, Temperature 428 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.1 MPa @Thickness 3.20 mm |
6260 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 10 % @Thickness 3.20 mm |
10 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 76.5 MPa @Thickness 3.20 mm |
11100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa @Thickness 3.20 mm |
370 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+6 - 1.00e+11 ohm | 1.00e+6 - 1.00e+11 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Abatron 440 A/B Filled Potting Compound (discontinued **)
- PolyOne Edgetek® AS-10GF/000 FR Acrylonitrile Butadiene Styrene (ABS), Glass/Carbon Fiber Filled (discontinue
- Momentive Performance Materials Siloprenâ„¢ LSR 2725/40 Liquid Silicone Rubber - Self-Bonding / Self-Lubricating
- SABIC Innovative Plastics LNP STAT-KON SC004 PA 12 (Europe-Africa-Middle East)
- SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66
- UBE 7034MT2 Nylon 6/12 Monofilament (Drawing Ratio=5.5)
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- ChevronTexaco URSA® SAE 20 Extra Duty
- Fibre Glast ProSet 125R / 229H Epoxy (discontinued **)
Copyright © lookpolymers.com All Rights Reserved